Organic light emitting display apparatus having thin-film encapsulation layer with interlayer and the manufacturing method thereof

ABSTRACT

An organic light emitting display apparatus includes a substrate, a display unit on the substrate, and a thin-film encapsulation layer for sealing the display unit, the thin-film encapsulation layer including a first organic film, a first inorganic film covering the first organic film, and an interlayer disposed at a lower surface of the first organic film, the interlayer defining an area where the first organic film is formed, an area of the interlayer being the same as the area of the first organic film.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority to and the benefit of Korean PatentApplication No. 10-2012-0149836, filed on Dec. 20, 2012, in the KoreanIntellectual Property Office, and entitled, “ORGANIC LIGHT EMITTINGDISPLAY APPARATUS AND THE MANUFACTURING METHOD THEREOF,” which isincorporated by reference herein in its entirety.

BACKGROUND

1. Field

Embodiments relate to an organic light emitting display apparatus and amanufacturing method thereof.

2. Description of the Related Art

An organic light emitting display apparatus may include an organic lightemitting device including a hole injection electrode, an electroninjection electrode, and an organic light emitting layer between theelectrodes. The organic light emitting display apparatus is aself-emitting type display device that generates light as excitons,which are generated by combination of holes (injected in the holeinjection electrode) and electrons (injected in the electron injectionelectrode) in the organic light emitting layer, fall from an exitedstate to a ground state.

The organic light emitting display apparatus, which is a self-emittingtype display apparatus, does not need a separate light source. As such,the organic light emitting display apparatus may be operated in a lowvoltage and formed in a light, thin form, and is becoming the center ofpublic attention as a next-generation display apparatus due to highquality properties such as a wide vision angle, a high contrast, a highresponse speed, etc.

SUMMARY

Embodiments are directed to an organic light emitting display apparatus,including a substrate, a display unit on the substrate, and a thin-filmencapsulation layer for sealing the display unit, the thin-filmencapsulation layer including a first organic film, a first inorganicfilm covering the first organic film, and an interlayer disposed at alower surface of the first organic film, the interlayer defining an areawhere the first organic film is formed, an area of the interlayer beingthe same as the area of the first organic film.

The interlayer may include one or more of an alkali metal salt or analkali earth metal salt.

The interlayer may include one or more of lithium fluoride, calciumfluoride, magnesium chloride, or sodium chloride.

The interlayer may have a thickness of about 50 Å to about 600 Å.

The organic light emitting display apparatus may further include asecond organic film on the first inorganic film, and a second inorganicfilm covering the second organic film.

The organic light emitting display apparatus may further include asecond interlayer for defining an area where the second organic film isformed, the second interlayer being between the first inorganic film andthe second organic film.

The organic light emitting display apparatus may further include a thirdinorganic film on the display unit, the interlayer being between thethird inorganic film and the first organic film.

The interlayer may be hydrophilic.

Embodiments are also directed to an organic light emitting displayapparatus, including a substrate, a display unit formed on thesubstrate, and a thin-film encapsulation layer for sealing the displayunit, the thin-film encapsulation layer including a plurality of organicfilms, a plurality of inorganic films alternately laminated with theplurality of organic films, and an interlayer formed on a lower surfaceof an organic film on at least a lowest layer among the organic films,the interlayer including one or more of an alkali metal salt or analkali earth metal salt.

The interlayer may include one or more of lithium fluoride, calciumfluoride, magnesium chloride, or sodium chloride.

The interlayer may define an area where the organic film on the lowestlayer is formed, and an area of the interlayer may be the same as thearea of the organic film on the lowest layer.

The interlayer may be formed on the lower surface of each of theplurality of organic films.

The interlayer may be hydrophilic.

The interlayer may contact the display unit.

Embodiments are also directed to a method of manufacturing an organiclight emitting display apparatus, the method including forming a displayunit on a substrate, and forming a thin-film encapsulation layer forsealing the display unit, the forming of the thin-film encapsulationlayer including forming an interlayer on the display unit, theinterlayer including at least one of an alkali metal salt and an alkaliearth metal salt, forming a first organic film corresponding to theinterlayer, and forming a first inorganic film to cover the firstorganic film, the first organic film being formed on only an area wherethe interlayer is formed.

The interlayer may have a thickness of about 50 Å to about 600 Å.

The interlayer may include one or more of lithium fluoride, calciumfluoride, magnesium chloride, or sodium chloride.

The method may further include forming a second organic film on thefirst inorganic film, and forming a second inorganic film to cover thesecond organic film.

The method may further include forming a second interlayer on the firstinorganic film before forming the second organic film. The secondorganic film may be formed on only an area where the second interlayeris formed.

The method may further include forming a third inorganic film to coverthe display unit before forming the interlayer.

The method may further include plasma-processing the third inorganicfilm before forming the interlayer.

BRIEF DESCRIPTION OF THE DRAWINGS

Features will become apparent to those of skill in the art by describingin detail example embodiments with reference to the attached drawings inwhich:

FIG. 1 is a cross-sectional diagram schematically illustrating anorganic light emitting display apparatus according to an exampleembodiment;

FIG. 2 is an enlarged cross-sectional diagram illustrating a displayunit of the organic light emitting display apparatus of FIG. 1;

FIGS. 3 and 4 are cross-sectional diagrams illustrating modifiedexamples of the organic light emitting display apparatus of FIG. 1; and

FIGS. 5 to 7 are cross-sectional diagrams schematically illustrating amethod of manufacturing the organic light emitting display apparatus ofFIG. 1.

DETAILED DESCRIPTION

Example embodiments will now be described more fully hereinafter withreference to the accompanying drawings; however, they may be embodied indifferent forms and should not be construed as limited to theembodiments set forth herein. Rather, these embodiments are provided sothat this disclosure will be thorough and complete, and will fullyconvey the scope of the example embodiments to those skilled in the art.

In the drawing figures, dimensions may be exaggerated for clarity ofillustration. It will be understood that when an element is referred toas being “on” another element, it can be directly on the other element,or one or more intervening elements may also be present. It will also beunderstood that when an element is referred to as being “under” anotherelement, it can be directly under, or one or more intervening elementsmay also be present. It will also be understood that when an element isreferred to as being “between” two elements, it can be the only elementbetween the two elements, or one or more intervening elements may alsobe present. In the case where a position relationship between two itemsare described with the terms “on ˜,” “on the top of ˜,” or the like, oneor more items may be interposed therebetween unless a description isgiven without the term “directly.” Like reference numerals refer to likeelements throughout.

As used herein, the term “and/or” includes any and all combinations ofone or more of the associated listed items. Expressions such as “atleast one of,” when preceding a list of elements, modify the entire listof elements and do not modify the individual elements of the list.

The terms such as “first” and “second” may be used to describe variouscomponents, but the components should not be limited by such terms. Theterms are used only to distinguish one component from another component.

FIG. 1 is a cross-sectional diagram schematically illustrating anorganic light emitting display apparatus according to an exampleembodiment, and FIG. 2 is an enlarged cross-sectional diagramillustrating a display unit of the organic light emitting displayapparatus of FIG. 1.

Referring to FIGS. 1 and 2, an organic light emitting display apparatus10 may include a substrate 100, a display unit 200 on the substrate 100,and an encapsulation layer 300 for sealing the display unit 200.

The substrate 100 may be a flexible substrate, and may be formed of,e.g., a plastic having superior heat-resistance and durability, such aspolyimide, polyethylene terephthalate (PET), polycarbonate, polyethylenenaphthalate, polyarylate (PAR), polyetherimide, etc. However,embodiments are not limited to these examples, and the substrate 120 maybe formed of a material such as metal, glass, etc.

The display unit 200 may include an organic thin-film transistor layer200 a and a pixel unit 200 b. The pixel unit 200 b may be an organiclight emitting device. Hereinafter, the display unit 200 will bedescribed in detail with reference to FIG. 2.

A buffer layer 212 may be formed on the substrate 100. The buffer layer212 may help prevent infiltration of impurities and other elementsthrough the substrate 100 and may help provide a flat plane on the upperside of the substrate, and may be formed of various materials forperforming such roles. For example, the buffer layer 212 may contain aninorganic material such as silicon oxide, silicon nitride, siliconoxynitride, aluminum oxide, aluminum nitride, titanium oxide, titaniumnitride, etc., or an organic material such as polyimide, polyester,acryl, etc., and/or may be formed of a laminate of such materials.

The thin-film transistor (TFT) layer 200 a may be formed on the bufferlayer 212. The present embodiment illustrates a top-gate type thin-filmtransistor as an example of the thin-film transistor layer 200 a, but athin-film transistor having a different structure may also be used.

The thin-film transistor layer 200 a may include an active layer 221, agate electrode 222, and source and drain electrodes 223.

In an implementation, the active layer 221 may be formed by asemiconductor material on the buffer layer 212, and a gate insulatingfilm 213 may be formed to cover the active layer 221. An inorganicsemiconductor, such as amorphous silicon or polysilicon, or an organicsemiconductor may be used as the active layer 221. The active layer 221may include a source region, a drain region, and a channel regionbetween the source region and the drain region. The gate insulating film213 may be used to insulate the active layer 221 from the gate electrode222, and may be formed of an organic material or an inorganic materialsuch as SiN_(x), SiO₂, etc.

The gate electrode 222 may be provided on the gate insulating film 213,and an interlayer insulating film 214 may be formed to cover the gateinsulating film 213.

The gate electrode 222 may contain, e.g., Au, Ag, Cu, Ni, Pt, Pd, Al,Mo, etc., and/or alloys such as Al:Nd and Mo: W, but the gate electrode222 is not limited to these examples.

The interlayer insulating film 214 may be disposed between the gateelectrode 222 and the source and drain electrodes 223 for insulationbetween the electrodes, and may be formed of an inorganic material suchas SiN_(x), SiO₂, etc.

The source and drain electrodes 223 may be formed on the interlayerinsulating film 214. The interlayer insulating film 214 and the gateinsulating film 213 may be formed to expose the source area and drainarea of the active layer 221, and the source and drain electrodes 223may be formed to contact the exposed source area and drain areas of theactive layer 221.

FIG. 2 illustrates a top-gate type thin-film transistor (TFT))sequentially including the active layer 221, the gate electrode 222, andthe source and drain electrode 223, but embodiments are not limited tothis example, and the gate electrode 222 may be disposed on the lowerpart of the active layer 221.

The thin-film transistor (TFT) layer 200 a may be electrically connectedto the pixel unit 200 b to operate the pixel unit 200 b, and may becovered by an overcoat film 215.

An inorganic insulating film and/or an organic insulating film may beused as the overcoat film 215. The inorganic insulating film mayinclude, e.g., SiO₂, SiN_(x), SiON, Al₂O₃, TiO₂, Ta₂O₅, HfO₂, ZrO₂, BST,PZT, etc., and the organic insulating film may include, e.g., a generalpolymer (PMMA, PS), a polymer derivative having a phenolic group, anacrylate polymer, an amide polymer, an aryl ether polymer, an amaidpolymer, a fluorinated polymer, a p-xylene polymer, a vinyl alcoholpolymer, a blend thereof, etc. The overcoat film 215 may also be formedof a composite laminate of an inorganic insulating film and an organicinsulating film.

The pixel unit 200 b may be formed on the overcoat film 215. The pixelunit 200 b may include a pixel electrode, an intermediate layer 232, anda counter electrode 233.

The pixel electrode 231 may be formed on the overcoat film 215 and maybe electrically connected to the source or drain electrode 223 through acontact hole 230 formed on the overcoat film 215.

The pixel electrode 231 may be a reflective electrode. The pixelelectrode 231 may include, e.g., Ag, Mg, Al, Pt, Pd, Au, Ni, Nd, Ir, Cr,an alloy thereof, etc. The pixel electrode 231 may be a reflective film.The pixel electrode 231 may be a transparent or semitransparentelectrode layer. The transparent or semitransparent electrode layer mayinclude one or more of indium tin oxide (ITO), indium zinc oxide (IZO),zinc oxide (ZnO), indium oxide (In₂O₃), indium gallium oxide (IGO), oraluminum zinc oxide (AZO).

The counter electrode 233 may be disposed to face the pixel electrode231 and may be a transparent or semitransparent electrode. The counterelectrode 233 may be formed of a metal thin film with small workfunction such as, e.g., Li, Ca, LiF/Ca, LiF/Al, Al, Ag, Mg, an alloythereof, etc. An auxiliary electrode layer or bus electrode may befurther formed of materials for a transparent electrode such as ITO,IZO, ZnO, or In₂O₃ on a metal thin film.

The counter electrode 233 may transmit light emitted from an organiclight emitting layer that is included in the intermediate layer 232.Light emitted from the organic light emitting layer may be reflecteddirectly or by the pixel electrode 231 formed of a reflective electrodeso as to be emitted to the counter electrode 233.

The organic light emitting display apparatus 10 of the presentembodiment is not limited to a front emitting type, and the organiclight emitting display apparatus 10 may also be a back emitting type, inwhich light emitted from the organic light emitting layer is emitted tothe substrate 100. In this case, the pixel electrode 231 may be formedof a transparent or semitransparent electrode, and the counter electrode233 may be formed of a reflective electrode. Further, the organic lightemitting display apparatus 10 of the present embodiment may be aboth-side emitting type that emits light in both front and backdirections.

A pixel definition layer 216 may be formed on the pixel electrode 231.The pixel definition layer 216 may expose a predetermined area of thepixel electrode 231, and the intermediate layer 232 including theorganic light emitting layer may be positioned in the exposed area.

The organic light emitting layer may be formed of, e.g., a low molecularweight organic material or a polymeric organic material. Theintermediate layer 232 may include a functional layer such as a holetransport layer (HTL), a hole injection layer (HIL), an electrontransport layer (ETL), and/or an electron injection layer (EIL) inaddition to the organic light emitting layer.

Referring to FIG. 1 again, the encapsulation layer 300 seals the displayunit 200 and may help prevent deterioration of the display unit 200. Theencapsulation layer 300 may include a first organic film 310, a firstinorganic film 320 covering the first organic film 310, and aninterlayer 330 formed on the lower surface of the first organic film310.

The first organic layer 310, for example, may be formed to cover thedisplay unit 200. The first organic layer 310 may be formed of anorganic material having flexibility such as polyurea or polyacrylate,and thus the first organic layer 310 may relax internal stress of theinorganic film 320 or enhance the effect of preventing permeation ofexternal moisture or oxygen by filling a fine crack and pin hole of theinorganic film 320.

The first inorganic film 320 may be formed of a moisture-resistantinorganic material such as SiN_(x), Al₂O₃, SiO₂, TiO₂, etc. The firstinorganic film 320 may be formed to cover the first organic film 310.

FIG. 1 illustrates that the encapsulation layer 300 includes the firstorganic film 310 and the first inorganic film 320, but embodiments arenot limited to this example, and the encapsulation layer 300 may beformed by alternate lamination of a plurality of organic films andinorganic films, and the inorganic film may be first formed to contactthe display unit 200, which will be described below with reference toFIGS. 3 and 4.

The interlayer 330 may include one or more of an alkali metal salt or analkali earth metal salt, which may be strongly bonded with a liquid typemonomer that may be used to form the first organic film 310. In animplementation, the interlayer 330 may include one or more of LiF, CaF₂,MgCl₂, or NaCl.

The interlayer 330 may be hydrophilic and define an area where the firstorganic film 310 is formed. For example, after the interlayer 330 isformed on the display unit 200, there may be an energy differencebetween an area where the interlayer 330 is formed and an area where theinterlayer is not formed. Thus, a liquid type monomer, which may be usedto form the first organic film 310, may be deposited only in the areawhere the interlayer 330 is formed.

The area of the first organic film 310 may be the same as the area ofthe interlayer 330. The first organic film 310 and the interlayer 330may be laterally coextensive. The interlayer 330 may clearly set aboundary where the first organic film 310 is formed. Thus, the firstorganic film 310 may be prevented from being exposed to the outside(e.g., as an edge tail), and thereby the side or lateral moistureresistance of the organic light emitting display apparatus 10 may beimproved, and a dead area of the organic light emitting displayapparatus 10 may be decreased.

The interlayer 330 may be formed with a thickness T of, e.g., about 50 Åto about 600 Å. If the thickness T of the interlayer 330 is smaller than50 Å, the interlayer 330 may not be uniformly formed, but may be formeddiscontinuously. For example, the interlayer 330 may be formed in anisland type, and thus there may be a defect in the first organic film310 formed on the interlayer 330. In contrast, if the thickness T of theinterlayer 330 is greater than 600 Å, the optical vision angle of theorganic light emitting display apparatus 10 may be changed, and theluminance of the organic light emitting display apparatus 10 may bedeteriorated as the unique color of the material contained in theinterlayer 330 is revealed. Hence, the interlayer 330 may be formed witha thickness of about 50 Å to about 600 Å.

FIGS. 3 and 4 are cross-sectional diagrams illustrating modifiedexamples of the organic light emitting display apparatus of FIG. 1.

Referring to FIG. 3, the organic light emitting display apparatus 10Bmay include the substrate 100, the display unit 200 formed on thesubstrate 100, and an encapsulation layer 300B that seals the displayunit 200. The substrate 100 and the display unit 200 have already beendescribed with reference to FIGS. 1 and 2, and thus details thereof willnot be repeated here.

The encapsulation layer 300B may include the first organic film 310, thefirst inorganic film 320 for covering the first organic film 310, asecond organic film 310B formed on the first inorganic film 320, and asecond inorganic film 320B for covering the second organic film 310B.

The encapsulation layer 300B may be formed by alternate lamination of aplurality of organic films 310 and 310B and inorganic films 320 and320B. Further, though not illustrated in the drawings, an organic layer(not shown) and an inorganic layer (not shown) may be further formed.Further, the interlayer 330 may be formed on the lower surface of thefirst organic film 310 of at least the lowest layer among a plurality oforganic films 310 and 310B. Penetration of external moisture or oxygeninto the display unit 200 may be more effectively prevented by limitingan area where the first organic film 310 closest to the display unit 200is formed.

A second interlayer 330B, for defining an area where the second organicfilm 310B is formed, may be further formed between the first inorganicfilm 320 and the second organic film 310B. The second interlayer 330Bmay be formed of the same material as that of the interlayer 330, andmay perform the same function as that of the interlayer 330. Thus, thesecond organic film 310B may be prevented from being extended to theouter block by clearly setting the boundary where the second organicfilm 310B is formed.

The organic light emitting display apparatus 10C of FIG. 4 may includethe substrate 100, the display unit 200 formed on the substrate 100, andan encapsulation layer 300C that seals the display unit 200. Thesubstrate 100 and the display unit 200 have already been described withreference to FIGS. 1 and 2, and thus details thereof will not berepeated here.

The encapsulation layer 300C of FIG. 4 may include the first organicfilm 310, the first inorganic film 320 for covering the first organicfilm 310, the interlayer 330 formed on the lower surface of the firstorganic film 310, and a third inorganic film 320C formed on the displayunit 200. The third inorganic film 320C may first be laminated, and thenthe first organic film 310 and the first inorganic film 320 may belaminated. The interlayer 330 may define the area where the firstorganic film 310 is formed and may be formed between the third inorganicfilm 320C and the first organic film 310.

In an implementation, the third inorganic film 320C may beplasma-processed so as to have a hydrophilic surface. A hydrophilicsurface for the third inorganic film 320C may improve bonding strengthwith the interlayer 330 formed on the third inorganic film 320C. Thethird inorganic film 320C may block plasma, and thus the pixel unit 200b of the display unit 200, etc. may be prevented from being damaged bythe plasma when plasma-processing.

The organic light emitting display apparatus 10C may further include thethin-film encapsulation layer (300B of FIG. 3) illustrated in FIG. 3.

FIGS. 5 to 7 are cross-sectional diagrams schematically illustrating amethod of manufacturing the organic light emitting display apparatus ofFIG. 1.

Referring to FIG. 5, the display unit 200 and the interlayer 330 may beformed on the substrate 100. The display unit 200 may have aconfiguration illustrated in FIG. 2 and various organic light emittingdisplays may be applied.

The interlayer 330 may be formed with a thickness of about 50 Å to about600 Å, and may include one or more of alkali metal salt or alkali earthmetal salt. For example, the interlayer 330 may include one or more ofLiF, CaF₂, MgCl₂, or NaCl. The interlayer 330 may be formed usingvarious deposition methods. To prevent damage to the display unit 200when the interlayer 330 is formed directly on the display unit 200, adeposition method that does not use plasma may be used.

Further, though not illustrated in the drawings, the third inorganicfilm (320C of FIG. 4) may be first formed to cover the display unit 200before forming the interlayer 330. If the third inorganic film (320C ofFIG. 4) is formed first, the third inorganic film (320C of FIG. 4) mayblock plasma, and thus methods of forming the interlayer 330 may bediversified. Further, after forming the third inorganic film (320C ofFIG. 4), a plasma processing for adding hydrophilic property to thethird inorganic film (320C of FIG. 4) may be performed to enhance thebonding strength with the interlayer 330.

After forming the interlayer 330, the first organic film 310 may beformed as in FIG. 6.

The first organic film 310 may be formed of, e.g., polyurea orpolyacrylate. It may be difficult for such materials to be promptlydeposited. Thus, method for the first organic film 310 may evaporateliquid type monomer so as to be deposited on the substrate 100, and thenmay irradiate ultraviolet rays so as to be polymerized.

The interlayer 330 may be formed of a material which may be easilybonded with a liquid type monomer, and the evaporated liquid typemonomer may be deposited only in the area where the interlayer 330 isformed. Hence, the boundary where the first organic film 310 is formedmay be clearly set, and thus the dead area of the organic light emittingdisplay apparatus (10 of FIG. 1) may be decreased. Further, theevaporated liquid type monomer may be prevented from being extended tothe side, and thus the lateral moisture resistant property of theorganic light emitting display apparatus (10 of FIG. 1) may be improved.

Next, as illustrated in FIG. 7, the first inorganic film 320 may beformed to cover the first organic film 310. The first inorganic film 320may be formed by, e.g., sputtering, atomic layer deposition, chemicalvapor deposition, etc. The first inorganic film 320 may include, e.g.,SiN_(x), SiO_(x), AlO_(x), SiC_(x)N_(y), SiO_(x)N_(y), amorphous carbon,InO_(x), YbO_(x), etc., but embodiments are not limited to theseexamples.

Further, though not illustrated in the drawings, after forming the firstinorganic film 320, the second organic film (310B of FIG. 3) and thesecond inorganic film (320B of FIG. 3) may be formed as illustrated inFIG. 3, and an organic layer (not shown) and an inorganic layer (notshown) may be further formed. Further, before the second organic film310B is formed, the second interlayer 330B for defining the area wherethe second organic film (310B of FIG. 3) is formed may be furtherformed.

By way of summation and review, an organic light emitting displayapparatus may be deteriorated by external moisture or oxygen. Thus, itmay be desirable to seal the organic light emitting device so as to helpprotect it from external moisture, oxygen, etc. A thin filmencapsulation (TFE) layer may be considered for sealing the organiclight emitting device. When forming an organic film and an inorganicfilm, a mask corresponding to the film is placed on a substrate and apattern may be formed. At this time, an organic material may seep into agap between the mask and the substrate. The encapsulation feature of theorganic film may significantly deteriorated compared to theencapsulation feature of the inorganic film, and thus if the organicmaterial were to seep into a gap between the substrate and the mask, anorganic film may be formed between an inorganic film and the substrateor between an inorganic film and an inorganic film, through which oxygenor moisture may infiltrate into a display unit.

As described above, embodiments relate to an organic light emittingdisplay apparatus, of which the side moistureproof property may beimproved, and a manufacturing method thereof. According to embodiments,when an organic film is formed, the formed area of the organic film maybe limited, and thus the side moistureproof property of the organiclight emitting display apparatus may be improved. As such, the sidedesiccative property of the organic light emitting display apparatus maybe improved.

Example embodiments have been disclosed herein, and although specificterms are employed, they are used and are to be interpreted in a genericand descriptive sense only and not for purpose of limitation. In someinstances, as would be apparent to one of ordinary skill in the art asof the filing of the present application, features, characteristics,and/or elements described in connection with a particular embodiment maybe used singly or in combination with features, characteristics, and/orelements described in connection with other embodiments unless otherwisespecifically indicated. Accordingly, it will be understood by those ofskill in the art that various changes in form and details may be madewithout departing from the spirit and scope of the present invention asset forth in the following claims.

What is claimed is:
 1. An organic light emitting display apparatus,comprising: a substrate; a display unit on the substrate; a thin-filmencapsulation layer for sealing the display unit, the thin-filmencapsulation layer including a first organic film, a first inorganicfilm covering the first organic film, and a first interlayer disposed atand contacting a lower surface of the first organic film, the firstinterlayer defining an area where the first organic film is formed, thefirst interlayer and the first organic film having the same area; asecond organic film on the first inorganic film; a second inorganic filmcovering the second organic film; and a second interlayer defining anarea where the second organic film is formed, the second interlayerbeing between the first inorganic film and the second organic film. 2.The organic light emitting display apparatus as claimed in claim 1,wherein the first interlayer includes one or more of an alkali metalsalt or an alkali earth metal salt.
 3. The organic light emittingdisplay apparatus as claimed in claim 1, wherein the first interlayerincludes one or more of lithium fluoride, calcium fluoride, magnesiumchloride, or sodium chloride, and the first organic film includes one ormore of a polyurea or a polyacrylate.
 4. The organic light emittingdisplay apparatus as claimed in claim 1, wherein the first interlayerhas a thickness of about 50 Å to about 600 Å.
 5. The organic lightemitting display apparatus as claimed in claim 1, further comprising athird inorganic film on the display unit, the first interlayer beingbetween the third inorganic film and the first organic film.
 6. Theorganic light emitting display apparatus as claimed in claim 1, whereinthe first interlayer is hydrophilic, the first interlayer defining anentire area occupied by the first organic film, the first interlayercontacting the first organic film continuously across the entire area.7. An organic light emitting display apparatus, comprising: a substrate;a display unit disposed on the substrate; a thin-film encapsulationlayer for sealing the display unit, the thin-film encapsulation layerincluding a plurality of organic films, the plurality of organic filmsincluding a first organic film and a second organic film, a plurality ofinorganic films alternately laminated with the plurality of organicfilms, the plurality of inorganic films including a first inorganic filmand a second inorganic film, and a first interlayer disposed at andcontacting a lower surface of the first organic film, the firstinterlayer including one or more of lithium fluoride, magnesiumchloride, or sodium chloride, wherein: the second organic film is on thefirst inorganic film, the second inorganic film covers the secondorganic film, and a second interlayer defines an area where the secondorganic film is formed, the second interlayer being between the firstinorganic film and the second organic film.
 8. The organic lightemitting display apparatus as claimed in claim 7, wherein the organicfilm that is contacted by the first interlayer includes one or more of apolyurea or a polyacrylate.
 9. The organic light emitting displayapparatus as claimed in claim 7, wherein the first interlayer defines anarea where the first organic film on the lowest layer is formed, and thefirst interlayer and the first organic film on the lowest layer have thesame area.
 10. The organic light emitting display apparatus as claimedin claim 7, wherein the first interlayer is disposed at and contacts thelower surface of each of the plurality of organic films.
 11. The organiclight emitting display apparatus as claimed in claim 7, wherein thefirst interlayer is hydrophilic.
 12. The organic light emitting displayapparatus as claimed in claim 7, wherein the first interlayer contactsthe display unit.